| APTIV™ FILMS 1000 |
| APTIV 1000 series films are the unfilled semi-crystalline films made from VICTREX™ PEEK polymer. The film provides a material solution for engineers in ultra-high performance applications. |
| Material Properties | |||
| Physical | Nominal Value | Unit | Test Method |
| Density (23°C) | 1.30 | g/cm³ | ISO 1183 |
| Water Absorption 1 (Equilibrium, 23°C, 0.0500 mm, 50% RH) | 0.040 | % | ISO 62 |
| Shrinkage MD 2 (200°C, 50.0 µm) | < 0.50 | % | |
| Shrinkage TD 2 (200°C, 50.0 µm) | < 0.50 | % | |
| Films | Nominal Value | Unit | Test Method |
| Film Thickness - Recommended / Available | 8 to 750 µm | | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 23°C, 25 µm | 2600 | MPa | |
| TD : 23°C, 25 µm | 2800 | MPa | |
| MD : 23°C, 50 µm | 2500 | MPa | |
| TD : 23°C, 50 µm | 2500 | MPa | |
| MD : 23°C, 125 µm | 2400 | MPa | |
| TD : 23°C, 125 µm | 2300 | MPa | |
| MD : 23°C, 250 µm | 2300 | MPa | |
| TD : 23°C, 250 µm | 2300 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 23°C, 25 µm | 140 | MPa | |
| TD : Break, 23°C, 25 µm | 120 | MPa | |
| MD : Break, 23°C, 50 µm | 130 | MPa | |
| TD : Break, 23°C, 50 µm | 120 | MPa | |
| MD : Break, 23°C, 125 µm | 120 | MPa | |
| TD : Break, 23°C, 125 µm | 120 | MPa | |
| MD : Break, 23°C, 250 µm | 110 | MPa | |
| TD : Break, 23°C, 250 µm | 110 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 23°C, 25 µm | > 150 | % | |
| TD : Break, 23°C, 25 µm | > 150 | % | |
| MD : Break, 23°C, 50 µm | > 150 | % | |
| TD : Break, 23°C, 50 µm | > 150 | % | |
| MD : Break, 23°C, 125 µm | > 150 | % | |
| TD : Break, 23°C, 125 µm | > 150 | % | |
| MD : Break, 23°C, 250 µm | > 150 | % | |
| TD : Break, 23°C, 250 µm | > 150 | % | |
| Trouser Tear Resistance 3 | ISO 6383-1 | ||
| MD : 50 µm | 6.00 | N/mm | |
| TD : 50 µm | 8.00 | N/mm | |
| Puncture Resistance (23°C, 50.0 µm) | 26 | kJ/m² | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
| CLTE - Flow 4 (0.0500 mm) | 4.7E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
| Volume Resistivity 5 (23°C, 50 µm) | 4.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 6 | ASTM D149 | ||
| 23°C, 25 µm | 270 | kV/mm | |
| 23°C, 50 µm | 190 | kV/mm | |
| 23°C, 125 µm | 120 | kV/mm | |
| 23°C, 250 µm | 70 | kV/mm | |
| Dielectric Constant (23°C, 50 µm, 10 MHz) | 3.5 | | ASTM D150 |
| Dissipation Factor (23°C, 50 µm, 10 MHz) | 2.0E-3 | | ASTM D150 |
| Dielectric Breakdown | ASTM D149 | ||
| 23°C, 25.0 µm | 6750 | V | |
| 23°C, 50.0 µm | 9500 | V | |
| 23°C, 125.0 µm | 15000 | V | |
| 23°C, 250.0 µm | 17500 | V | |
| Notes |
| 124 hrs |
| 2TM-VX-84 |
| 323°C |
| 4below Tg |
| 5100 V |
| 60.25 inch electrode |