APTIV 薄膜 1000 系列

APTIV™ FILMS 1000

APTIV 1000 series films are the unfilled semi-crystalline films made from VICTREX™ PEEK polymer. The film provides a material solution for engineers in ultra-high performance applications.

APTIV films are a comprehensive range of versatile, high-performance films, the use of which can facilitate reduced systems costs, improved performance and enhanced design freedom.

APTIV 1000 has a unique combination of properties providing high temperature performance, light weight, mechanical strength, durability, excellent radiation, hydrolysis and chemical resistance, electrical insulation, wear and abrasion resistance, excellent barrier properties with high purity, good flammability without the use of flame retardants, low toxicity of combustion products, and low moisture absorption in a film format. Inherently halogen free and ease of processing makes APTIV films a technology enabler for our customers and end users.

Request a quote Download PDF

Material Properties
Physical	Nominal Value	Unit	Test Method
Density (23°C)	1.30	g/cm³	ISO 1183
Water Absorption¹ (Equilibrium, 23°C, 0.0500 mm, 50% RH)	0.040	%	ISO 62
Shrinkage MD² (200°C, 50.0 µm)	< 0.50	%
Shrinkage TD² (200°C, 50.0 µm)	< 0.50	%
Films	Nominal Value	Unit	Test Method
Film Thickness - Recommended / Available	8 to 750 µm
Tensile Modulus			ISO 527-3
MD : 23°C, 25 µm	2600	MPa
TD : 23°C, 25 µm	2800	MPa
MD : 23°C, 50 µm	2500	MPa
TD : 23°C, 50 µm	2500	MPa
MD : 23°C, 125 µm	2400	MPa
TD : 23°C, 125 µm	2300	MPa
MD : 23°C, 250 µm	2300	MPa
TD : 23°C, 250 µm	2300	MPa
Tensile Stress			ISO 527-3
MD : Break, 23°C, 25 µm	140	MPa
TD : Break, 23°C, 25 µm	120	MPa
MD : Break, 23°C, 50 µm	130	MPa
TD : Break, 23°C, 50 µm	120	MPa
MD : Break, 23°C, 125 µm	120	MPa
TD : Break, 23°C, 125 µm	120	MPa
MD : Break, 23°C, 250 µm	110	MPa
TD : Break, 23°C, 250 µm	110	MPa
Tensile Elongation			ISO 527-3
MD : Break, 23°C, 25 µm	> 150	%
TD : Break, 23°C, 25 µm	> 150	%
MD : Break, 23°C, 50 µm	> 150	%
TD : Break, 23°C, 50 µm	> 150	%
MD : Break, 23°C, 125 µm	> 150	%
TD : Break, 23°C, 125 µm	> 150	%
MD : Break, 23°C, 250 µm	> 150	%
TD : Break, 23°C, 250 µm	> 150	%
Trouser Tear Resistance³			ISO 6383-1
MD : 50 µm	6.00	N/mm
TD : 50 µm	8.00	N/mm
Puncture Resistance (23°C, 50.0 µm)	26	kJ/m²	Internal Method
Thermal	Nominal Value	Unit	Test Method
CLTE - Flow ⁴ (0.0500 mm)	4.7E-5	cm/cm/°C	ASTM D696
Electrical	Nominal Value	Unit	Test Method
Volume Resistivity⁵ (23°C, 50 µm)	4.0E+16	ohms·cm	ASTM D257
Dielectric Strength⁶			ASTM D149
23°C, 25 µm	270	kV/mm
23°C, 50 µm	190	kV/mm
23°C, 125 µm	120	kV/mm
23°C, 250 µm	70	kV/mm
Dielectric Constant (23°C, 50 µm, 10 MHz)	3.5		ASTM D150
Dissipation Factor (23°C, 50 µm, 10 MHz)	2.0E-3		ASTM D150
Dielectric Breakdown			ASTM D149
23°C, 25.0 µm	6750	V
23°C, 50.0 µm	9500	V
23°C, 125.0 µm	15000	V
23°C, 250.0 µm	17500	V

Notes

¹24 hrs

²TM-VX-84

³23°C

⁴below Tg

⁵100 V

⁶0.25 inch electrode