Go back to datasheets

VICTREX FG™ POLYMER 100/101

High performance Food Grade thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding, colour natural/beige (100) and black (101).

The VICTREX FG™ 100 family of materials is intended for applications needing mechanical properties at ambient and elevated temperatures along with long-term creep resistance, point and edge retention and low coefficient of thermal expansion for metal replacement. Chemically resistant to aggressive environments, suitable for sterilisation.

Material Properties
Physical

Nominal Value

Unit

Test Method

Density (Crystalline)

1.30

g/cm³

ISO 1183

Spiral Flow 1

22.0

cm

Internal Method

Molding Shrinkage 2

ISO 294-4

Across Flow

1.3

%

Flow

1.0

%

Water Absorption (Saturation, 23°C)

0.45

%

ISO 62

Water Absorption - Saturation (100°C)

0.55

%

ISO 62
Mechanical

Nominal Value

Unit

Test Method

Tensile Stress (Yield, 23°C)

105

MPa

ISO 527-2

Tensile Strain (Break, 23°C)

20

%

ISO 527-2

Flexural Modulus (23°C)

3900

MPa

ISO 178

Flexural Stress (Yield, 23°C)

175

MPa

ISO 178

Compressive Stress (23°C)

130

MPa

ISO 604
Impact

Nominal Value

Unit

Test Method

Notched Izod Impact Strength (23°C)

5.0

kJ/m²

ISO 180/A

Unnotched Izod Impact Strength (23°C)

No Break

ISO 180
Hardness

Nominal Value

Unit

Test Method

Shore Hardness (Shore D, 23°C)

85.0

ISO 868
Thermal

Nominal Value

Unit

Test Method

Deflection Temperature Under Load (1.8 MPa, Unannealed)

156

°C

ISO 75-2/Af

Glass Transition Temperature

ISO 11357-2

Onset

143

°C

Midpoint

147

°C

Melting Temperature

343

°C

ISO 11357-3

CLTE - Flow

ISO 11359-2

< 143°C

50

ppm/K

> 143°C

120

ppm/K

CLTE - Average

ISO 11359-2

< 143°C

55

ppm/K

> 143°C

140

ppm/K

Thermal Conductivity 3 (23°C)

0.29

W/m/K

ISO 22007-4
Electrical

Nominal Value

Unit

Test Method

Volume Resistivity (23°C)

1.0E+16

ohms·cm

IEC 60093

Dielectric Strength (2.00 mm)

23.0

kV/mm

IEC 60243-1
Typical Processing Information
Injection

Nominal Value

Unit

Drying Temperature

120 to 150

°C

Drying Time

3.0 to 5.0

hr

Suggested Max Moisture

0.020

%

Hopper Temperature

< 100

°C

Rear Temperature

350

°C

Middle Temperature

355

°C

Front Temperature

360

°C

Nozzle Temperature

365

°C

Mould Temperature

160 to 200

°C

Injection Notes

Runner: Die / nozzle >3mm, manifold >3.5mm
Gate: >1mm or 0.5 x part thickness

Important notes:
1) Processing conditions quoted in our datasheets are typical of those used in our processing laboratories

  • Data for mould shrinkage should be used for material comparison. Actual mould shrinkage values are highly dependent on part geometry, mould configuration, and processing conditions.
  • Mould shrinkage differs for along flow and across flow directions. “Along flow” direction is taken as the direction the molten material is travelling when it exits the gate and enters the mould.
  • Mould shrinkage is expressed as a percent change in dimension of a specimen in relation to mould dimensions.

2) Data are generated in accordance with prevailing national, international and internal standards, and should be used for material comparison. Actual property values are highly dependent on part geometry, mould configuration and processing conditions. Properties may also differ for along flow and across flow directions.

Detailed data available on our website www.victrex.com or upon request.

Notes
1Mould Temperature: 160°C, Melt Temperature: 365°C, 1.00 mm
2365°C nozzle, 160°C tool
3Average