APTIV XPI™ フィルム A105
| APTIV XPI™ FILMS A105 |
| APTIV XPI™ Film A105 is an unfilled semi-crystalline film made from VICTREX™ PEEK polymer. The film provides durability and reliability in the most demanding application environments by incorporating all of the outstanding properties of VICTREX™ PEEK ( PolyEtherEtherKetone) polymer in a thin film format. It is typically used as high-voltage e-motor stator insulation, enabling excellent thermal management as well as high electrical performance and maximised copper fill factor, resulting in enhanced e-motor efficiency. |
| Material Properties | |||
| Physical | Nominal Value | Unit | Test Method |
| Density 1 (23°C) | 1.30 | g/cm³ | ISO 1183 |
| Water Absorption 2 (Equilibrium, 23°C, 0.0500 mm, 50% RH) | 0.040 | % | ISO 62 |
| Shrinkage MD 3 (200°C, 50.0 µm) | < 0.50 | % | |
| Shrinkage TD 3 (200°C, 50.0 µm) | < 0.50 | % | |
| Films | Nominal Value | Unit | Test Method |
| Film Thickness - Recommended / Available | 100 µm | | |
| Tensile Modulus | ISO 527 | ||
| MD : 23°C, 100 µm | 2400 | MPa | |
| TD : 23°C, 100 µm | 2300 | MPa | |
| Tensile Stress | ISO 527 | ||
| MD : Break, 23°C, 100 µm | 120 | MPa | |
| TD : Break, 23°C, 100 µm | 120 | MPa | |
| Tensile Elongation | ISO 527 | ||
| MD : Break, 23°C, 100 µm | > 150 | % | |
| TD : Break, 23°C, 100 µm | > 150 | % | |
| Thermal | Nominal Value | Unit | Test Method |
| Glass Transition Temperature (Onset) | 143 | °C | ISO 11357 |
| Melting Temperature | 343 | °C | ISO 11357 |
| CLTE - Flow 4 (0.0500 mm) | 3.5E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity 5 | 0.25 | W/m/K | ASTM E1461 |
| RTI Elec | 240 | °C | UL 746B |
| Electrical | Nominal Value | Unit | Test Method |
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (CTI) 6 | PLC 4 | | IEC 60112 |
| Breakdown Voltage 7 (23°C) | 16.2 | kV | ASTM D149 |
| Breakdown Voltage Retention 8 (180°C) | > 95.0 | % | IEC 60243 |
| Dielectric Constant 9 (23°C) | 3.20 | | IEC 60250 |
| Dissipation Factor 10 | 3.0E-3 | | IEC 60250 |
| Partial Discharge Inception Voltage | IEC 60270 | ||
| 23°C | 1199 | V | |
| 180°C | 890 | V | |
| Additional Information | |||
| Product Dimensions | |||
| Notes |
| 1Crystalline |
| 224 hrs |
| 3TM-VX-84 |
| 4Below Tg |
| 5Through Plane |
| 623°C |
| 71 kV/s |
| 8180 °C, 500 V/s |
| 91 kHz |
| 101MHz |