APTIV 필름 1102 시리즈

APTIV 1100 series films are the mineral filled semi-crystalline films made from VICTREX™ PEEK polymer. The film provides a material solution for engineers in ultra-high performance applications.

APTIV films are a comprehensive range of versatile, high-performance films, the use of which can facilitate reduced systems costs, improved performance and enhanced design freedom.

APTIV 1100 has a unique combination of properties providing high temperature performance, mechanical strength, durability, excellent radiation, hydrolysis and chemical resistance, electrical insulation, excellent barrier properties with high purity, good flammability without the use of flame retardants, low toxicity of combustion products, and low moisture absorption in a film format. Inherently halogen free and ease of processing makes APTIV films a technology enabler for our customers and end users. APTIV 1100 series provides a higher modulus and lower coefficient of linear thermal expansion over the APTIV 1000 series.

Material Properties
Physical	Nominal Value	Unit	Test Method
Density (23°C)	1.45	g/cm³	ISO 1183
Water Absorption¹ (Equilibrium, 23°C, 0.0500 mm, 50% RH)	0.080	%	ISO 62
Shrinkage MD² (200°C, 50.0 µm)	< 0.50	%
Shrinkage TD² (200°C, 50.0 µm)	< 0.50	%
Films	Nominal Value	Unit	Test Method
Film Thickness - Recommended / Available	12 to 125 µm
Tensile Modulus			ISO 527-3
MD : 23°C, 25 µm	5000	MPa
TD : 23°C, 25 µm	4500	MPa
MD : 23°C, 50 µm	4800	MPa
TD : 23°C, 50 µm	4300	MPa
MD : 23°C, 100 µm	4500	MPa
TD : 23°C, 100 µm	4200	MPa
Tensile Stress			ISO 527-3
MD : Break, 23°C, 25 µm	100	MPa
TD : Break, 23°C, 25 µm	80.0	MPa
MD : Break, 23°C, 50 µm	100	MPa
TD : Break, 23°C, 50 µm	80.0	MPa
MD : Break, 23°C, 100 µm	100	MPa
TD : Break, 23°C, 100 µm	80.0	MPa
Tensile Elongation			ISO 527-3
MD : Break, 23°C, 25 µm	> 100	%
TD : Break, 23°C, 25 µm	> 10	%
MD : Break, 23°C, 50 µm	> 100	%
TD : Break, 23°C, 50 µm	> 10	%
MD : Break, 23°C, 100 µm	> 100	%
TD : Break, 23°C, 100 µm	> 10	%
Trouser Tear Resistance³			ISO 6383-1
MD : 50 µm	6.00	N/mm
TD : 50 µm	7.00	N/mm
Puncture Resistance (23°C, 50.0 µm)	5	kJ/m²	Internal Method
Thermal	Nominal Value	Unit	Test Method
CLTE - Flow ⁴ (0.0500 mm)	3.5E-5	cm/cm/°C	ASTM D696
Thermal Conductivity			ASTM E1461
--⁵	0.43	W/m/K
--⁶	0.91	W/m/K
Electrical	Nominal Value	Unit	Test Method
Volume Resistivity⁷ (23°C, 50 µm)	1.0E+16	ohms·cm	ASTM D257
Dielectric Strength⁸ (23°C, 50 µm)	200	kV/mm	ASTM D149
Dielectric Constant (23°C, 50 µm, 10 MHz)	3.6		ASTM D150
Dissipation Factor (23°C, 50 µm, 10 MHz)	1.0E-3		ASTM D150

Notes

¹24 hrs

²TM-VX-84

³23°C

⁴below Tg

⁵Through Plane

⁶In-Plane

⁷100 V

⁸0.25 inch electrode