APTIV FILMS 1300 Serie - Schwarz
| APTIV™ FILMS 1300 |
| APTIV 1300 film is the black version of unfilled semi-crystalline films made from VICTREX™ PEEK polymer. The film provides a material solution for engineers in ultra-high performance applications offering an alternative option to the APTIV 1000 natural product. |
| Material Properties | |||
| Physical | Nominal Value | Unit | Test Method |
| Density (23°C) | 1.30 | g/cm³ | ISO 1183 |
| Shrinkage MD 1 (200°C, 50.0 µm) | < 2.0 | % | |
| Shrinkage TD 1 (200°C, 50.0 µm) | < 2.0 | % | |
| Films | Nominal Value | Unit | Test Method |
| Film Thickness - Recommended / Available | 50 to 100 µm | | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 23°C, 50 µm | 2500 | MPa | |
| TD : 23°C, 50 µm | 2500 | MPa | |
| MD : 23°C, 100 µm | 2400 | MPa | |
| TD : 23°C, 100 µm | 2300 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 23°C, 50 µm | 120 | MPa | |
| TD : Break, 23°C, 50 µm | 110 | MPa | |
| MD : Break, 23°C, 100 µm | 120 | MPa | |
| TD : Break, 23°C, 100 µm | 110 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 23°C, 50 µm | > 150 | % | |
| TD : Break, 23°C, 50 µm | > 150 | % | |
| MD : Break, 23°C, 100 µm | > 150 | % | |
| TD : Break, 23°C, 100 µm | > 150 | % | |
| Electrical | Nominal Value | Unit | Test Method |
| Volume Resistivity 2 (23°C, 50 µm) | 4.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 3 (23°C, 50 µm) | 190 | kV/mm | ASTM D149 |
| Notes |
| 1TM-VX-84 |
| 2100 V |
| 30.25 inch electrode |